Lushan@EF-3A It is a maleic acid grafted polyethylene product, used as a halogen-free flame retardant wire and cable compatibilizer, which can enhance the compatibility of resin matrix and flame retardant fillers (such as inorganic fillers such as ATH, CaO or MgOH), and improve the mechanical strength and toughness of the product. In addition, it is also applicable to wood-plastic products. At the same time, it can also be used as an adhesive in the application of five-layer co-extrusion blowing film for bonding PE and PA, EVOH resins.
Specification
| Project | Typical value | Test method |
| Appearance | Natural or light yellow particles | Diurnal vision |
| Density | 0.921 g/cm3 | ASTM D792 |
| Melt index (190 ° c/2.16 Kg) | 1.0 g/10min | ASTM D1238 |
| Melting point (DSC) | 121°C | ASTM D3418 |
| Vicat softening point | 92°C | ASTM D1525 |
Tensile strength | > 10 MPa | ASTM D638 |
| Elongation at break | > 600 % | ASTM D638 |
Production