Ceramic filter plate

Ceramic Filter Plate is a kind of large porous ceramic disc which is fired by inorganic membrane making technology. It has following characteristics: large filter area, high intensity and even aperture. Besides, the aperture size can be adjusted according to actual demands. The basic material is alumina, it has good resistance to acid and alkali. After a period of application, the Ceramic Filter plate can be cleaned by cycle reverse cleaning, ultrasonic and chemical cleaning agent and so on, to let the plates work with high efficiency.
Regarding firing process, traditionally the ceramic plate is consisted of two layers of plates which are glued together to form inner channels.But after long term running, the glue will block the pores to cause "flower spots"on the surface of the plates.
Considering this phenomenon, our company independently developed a new technology.Now the ceramic plate is poured in one mould as a whole（We select a kind of special material,when firing under high temperature, this material is volatilized to form the inner channels.）Thus, the"flower spots"will be avoided,also the ceramic plates will have higher strength and not easy to be broken.
Recently, for mine production decreased obviously after several times ore absorption,our company developed a new type of membrane surface.The porosity of the new membrane can reach 55.60%, the microporous inwalls are smooth, and the tiny particles can pass smoothly in ore absorption process, so the jams will be reduced better. Meanwhile,after long-term use and backwash, the regeneration ability is obvious, the service life is longer,so as to achieve the maximum efficiency of plate surface,and improve the output
Technical Date of separator machine
1.Filter flux(water pressure0.1Mpa): 1200-1800kg/h.m2
2.Recoil atmospheric pressure(in damp environment): the minimum is 0.6Mpa
3.Back wash pressure:the maximum is 0.3Mpa
4.Combined cleaning pressure of ultrasonic and chemical agent:the maximum is 0.2Mpa
5.Pore diameter range of membrane surface: 0.1µm-15µm
6.Dry weight of processed materials: 0.6-1.6t/h.m2